Maximum Thickness of Chrome Plating on Hydraulic Shaft

Q. Sir, What should be the maximum thickness of chrome plating on hydraulic shaft to get maximum life without chipping off?

A. Hard chrome usually behaves well in the 0.0005 to 0.010 thick range. Most aircraft hydraulic requirements are in the 0.003 to 0.005 thick range after chrome grinding. You don't need a lot of chrome to do the good work of sealing and wear resistance. Theoretically you can put on much more thickness upwards of 0.025 - 0.030 for certain salvage requirements. But those events should be carefully evaluated and used only on a limited basis.

Chipping is a sign of poor adhesion. If you are referring to chipping the edges, the problem can usually be resolved by better masking and anode design techniques. If you are referring to "chipping" of the chrome coating on the working surface of a hydraulic shaft, then we are more likely getting into issues with process control.

Specifically 1. "preparation" of the base metal 2. Current Density 3. Bath chemistry and temperature.

As usual in hard chrome plating, there is probably no simple answer.

I hope this brief response is helpful. Advise.

Randy Taylor

 

 

 

 


The information contained in this site is provided for your review and convenience. It is not intended to provide legal advice with respect to any federal, state, or local regulation.
You should consult with legal counsel and appropriate authorities before interpreting any regulations or undertaking any specific course of action.

Please note that many of the regulatory discussions on STERC refer to federal regulations. In many cases, states or local governments have promulgated relevant rules and standards
that are different and/or more stringent than the federal regulations. Therefore, to assure full compliance, you should investigate and comply with all applicable federal, state and local regulations.